Dead burned magnesia (DBM) is mainly made of natural magnesite ore with 46% content, which is calcined by high temperature kiln at about 1400℃-1800℃. Dead burned magnesia is mainly used as raw material for making magnesia bricks and producing amorphous refractory materials. The finished products are used in steel making, electric furnace bottom and ramming furnace.

Fused magnesia (FM) is a general term for the products of magnesia raw materials such as magnesite after high temperature treatment to the degree of sintering. The main varieties have 94%-98% content. Fused magnesia is a general term for the products of magnesia raw materials such as magnesite after high temperature treatment to the degree of sintering. The main varieties have 94%-98% content. Using high-temperature equipment such as shaft kilns and rotary kilns for one-time or two-step calcination.

Caustic calcined magnesia (CCM) is reactive form of MgO produced by firing magnesite at temperatures between 600°C - 1000°C. Mainly used in: Agricultural applications, Hydrometallurgical processes, Pulp and paper, Construction and Sorel cement, Chemicals and pharmaceuticals industry, Environmental applications, Glass industry.

Light burnt magnesia ball is made of magnesium oxide as the main raw material, adding water and binder at the same time, stirring and pressing under high pressure.

With the Light burnt magnesia ball, the slag is easy to combine with the lining, forming an effective slag protection layer on the lining, improving the life of the lining and reducing the consumption.

Refractory Bricks such as Magnesia Brick is mainly used for furnace lining, furnace bottom and furnace wall, oxygen converter permanent lining, non-ferrous metal smelting furnace, high temperature tunnel kiln, calcined magnesia and cement rotary kiln lining, furnace bottom and furnace wall, glass furnace regenerative lattice Bricks, etc.